Why CleanWRX 207® Is the Ultimate Rust Inhibitor for Blasting Jobs
Visual cleanliness isn't enough. Beneath the surface, non-visible contamination like chlorides, sulfates, and nitrates are eating away at your coating system's lifespan. CleanWRX 207® is engineered to eliminate these threats—before flash rust, adhesion failure, or blistering compromise your job.
Why Surface Contamination Matters
- Reduces coating lifespan
- Promotes rust and corrosion
- Causes osmotic blistering and poor adhesion
- Accelerates coating failure—even when the surface looks clean
Even trace levels of chlorides or other soluble salts can trigger flash rust or coating delamination. 207® doesn't just meet spec—it exceeds it.
What Makes CleanWRX 207® Different
- One-step process: Washes away non-visible contamination at the molecular level
- Prevents flash rust: Maintains visual standard for 3+ days, even in humid environments
- Zero residue: No films, no interference with coating bond
- No purified water required: Works with potable water (50:1) or DI/RO water (100:1)
- Will not foul pumps or filters: No downtime from clogs or cleanup
Application Versatility
- UHP waterjet
- Wet abrasive blasting
- High-power pressure washing
- Pump sprayers
Real Jobsite Results
In a controlled test, two steel panels were blasted with 30/60 garnet on April 4, 2025. One was left untreated, and the other was rinsed immediately with CleanWRX 207® at a 50:1 dilution. Both were left in a high-humidity shop environment in Oklahoma.
As of July 22, 2025, the untreated panel showed visible flash rust. The treated panel? Still clean—aside from the spot intentionally touched with a bare finger.
Don’t Let Contamination Destroy Your Coating Job
CleanWRX 207® removes what the eye can’t see and protects what your coating is meant to shield. Contact Sandblast Solutions Inc. today for application advice, availability, or to request a quote.